galvanized iron section properties tables
does anyone know of a resource on galvanized iron shapes tables? any leads will be appreciated.

are you talking about normal structural shapes which are galvanized?
yes, i would like to know if there are any factors that increase or decrease allowable stresses.
rarebug,
by your posts i assume you are talking about structural steel, not iron.
for normal structural grade steel (36 ksi to 50 ksi) the galvanising process does not have any significant effects on the properties. design them as per normal steel sections.
check out
yes, i was thinking about steel (iron plus carbon galvanized)
thank you csd72!!

__________________
借用达朗贝尔的名言：前进吧，你会得到信心!
[url="http://www.dimcax.com"]几何尺寸与公差标准[/url]

2009-09-09, 02:16 PM	#1
huangyhg 超级版主注册日期: 04-03 帖子: 18592 精华: 36 现金: 249466 标准币资产: 1080358888 标准币	galvanized iron section properties tables galvanized iron section properties tables does anyone know of a resource on galvanized iron shapes tables? any leads will be appreciated. are you talking about normal structural shapes which are galvanized? yes, i would like to know if there are any factors that increase or decrease allowable stresses. rarebug, by your posts i assume you are talking about structural steel, not iron. for normal structural grade steel (36 ksi to 50 ksi) the galvanising process does not have any significant effects on the properties. design them as per normal steel sections. check out yes, i was thinking about steel (iron plus carbon galvanized) thank you csd72!! __________________ 借用达朗贝尔的名言：前进吧，你会得到信心! [url="http://www.dimcax.com"]几何尺寸与公差标准[/url]